Common chemical, physical properties:
Composition | Montmorillonite derivative | organic ammonium |
Appearance | Light white fine powder | |
Moisture content (%) | ≤ 3.50 | |
Dry powder fineness (through mesh 200) | ≥ 99.0 | |
Loss on ignition (900℃ ，%) | 30.0~32.5 | |
Usage:
The 801-C product requires the high shear condition and the polarity activator to enhance its dispersion and viscosity reinforcement.
Pre-gel method:
item | 8% | 10% | Dispersion Condition |
Solvent | 89.4% | 86.7% | |
801-C | 8% | 10% | Medium speed mix, slow addition, high speed dispersion for 5~10 minutes |
Ethanol 95% | 2.6% | 3.3% | Dispersed in high speed 15~30 minutes |
This pre-gel could be added at any step of adjustment procedure, still the best time is before grinding.
Dry powder addition:
801C could be added as dry powder, it still needs polar activator to improve dispersing and thickening properties.
• Add resin/solvent
• Add 801-C, disperse in high speed for 5~10 minutes
• Add polar activator (Ethanol or Acetone with 5% water), high speed disperse for 15~20 minutes
• Add wetting agent, pigment, grind and disperse (whipping, ball-milling, sanding) to the required fineness
• Add other materials in system, disperse continuously to be average
Applications:
All solvent paint and coatings , sealing compounds, Iubricating grease and cast coatings ,etc.
Common chemical, physical properties:
Composition | Montmorillonite derivative | organic ammonium |
Appearance | Light white fine powder | |
Moisture content (%) | ≤ 3.50 | |
Dry powder fineness (through mesh 200) | ≥ 99.0 | |
Loss on ignition (900℃ ，%) | 30.0~32.5 | |
Usage:
The 801-C product requires the high shear condition and the polarity activator to enhance its dispersion and viscosity reinforcement.
Pre-gel method:
item | 8% | 10% | Dispersion Condition |
Solvent | 89.4% | 86.7% | |
801-C | 8% | 10% | Medium speed mix, slow addition, high speed dispersion for 5~10 minutes |
Ethanol 95% | 2.6% | 3.3% | Dispersed in high speed 15~30 minutes |
This pre-gel could be added at any step of adjustment procedure, still the best time is before grinding.
Dry powder addition:
801C could be added as dry powder, it still needs polar activator to improve dispersing and thickening properties.
• Add resin/solvent
• Add 801-C, disperse in high speed for 5~10 minutes
• Add polar activator (Ethanol or Acetone with 5% water), high speed disperse for 15~20 minutes
• Add wetting agent, pigment, grind and disperse (whipping, ball-milling, sanding) to the required fineness
• Add other materials in system, disperse continuously to be average
Applications:
All solvent paint and coatings , sealing compounds, Iubricating grease and cast coatings ,etc.